  Cathodic Electrodeposition and Characterization of YAG Nanostructure: Effect Current Density on the Morphology
M. Hosseinifard*, K. Ahmadi and A. Badiei
( Received: January 03, 2019 – Accepted in Revised Form: February 26, 2019 )

Abstract    Abstract YAG (Yttrium Aluminum Garnet) was successfully prepared through cathodic electrodeposition process using applying different current densities to the mixture of YCl3 and AlCl3 dissolved in water/ethanol 1:1 solution. Hydroxide precursors were cathodically grown on the cathode surface (at different current densities) and then the obtained hydroxide powder was heat-treated at 1100 °C for 4 h. The oxide products were characterized by XRD, FTIR, DSC-TGA, SEM and EDAX techniques. The effect of applied current density on the morphology and particle size of YAG nanostructures were investigated through SEM images. Results showed that the cathodic electrodeposition followed by heat-treatment can be used as a facile method for preparation of YAG nanostructures with different morphologies.


Keywords    Yttrium aluminum garnet, Nanostructure, Cathodic electrodeposition, Hydroxide